Experiments in landscapes

Lorem ipsum dolor sit amet consectetur. Adipiscing commodo facilisis volutpat eget iaculis amet sed arcu. Tortor arcu viverra eu non augue. Sapien id et mi libero vel. Sed tristique risus donec iaculis id euismod in rhoncus sapien.

Lorem ipsum dolor sit amet consectetur. Adipiscing commodo facilisis volutpat eget iaculis amet sed arcu. Tortor arcu viverra eu non augue.

Lorem ipsum dolor sit amet consectetur. Adipiscing commodo facilisis volutpat eget iaculis amet sed arcu. Tortor arcu viverra eu non augue.

Adding 3d models

Sea floor detailing

Central focal point added

using xxxxxxxxxx i sculpted a kraken after debate between the ideas of a sea serpant and a kraken. Thus i laid it in the ceenter, that i left blank so i could fill it later.

Painting the kraken

resine pore

as anyone who has worked with resine will know it is a tempremental and finicky material having to be at a sertain temperature constantly for the 2-3 days it takes to dry or a cascade exothermic reaction will ocure even when begining to dry it can reach upwards of 50 degrees celsius this isnt even a runaway exothermic reaction, a run away reaction can easily reach 100 degrees celsius more than enough to melt most plastic. to prevent this the air temperature should be around 23-28 degrees.

It is to be mentioned that if anything gose wronge it will eather explode or melt.

neadles to say something went wrong we believe it is due to a large aamount of air being traped in the base of the model and the heat of the resin caused slight cracks and holes to form expeling the air and leting in the resin causing the serfis deformations and captured resin bubles one the serfice. bubles are goten ride of by blowtorching them causing the resin to go back to liquid and not harden with the bubles. the floating brown bubbles where caused by them catching fire during this process.

due to the pigment in the resin not settling corectly the resin is sagnificantly darker than it should be withe the first layer having set perfectly but the second layer put undo stress on it and the bass bending the pilars in wards. This is the main problem that caused the sagnificant deformation on the serface.

Sanding down the resine